Failure analysis of CFRP laminates subjected to Compression After Impact: FE simulation using discrete interface elements

Samuel Rivallant (1) , Christophe Bouvet (1) , Natthawat Hongkarnjanakul (1)

1 ICA - Institut Clément Ader

This paper presents a model for the numerical simulation of impact damage, permanent indentation and compression after impact (CAI) in CFRP laminates. The same model is used for the formation of damage developing during both low-velocity / low-energy impact tests and CAI tests. The different impact and CAI elementary damage types are taken into account, i.e. matrix cracking, fiber failure and interface delamination. Experimental tests and model results are compared, and this comparison is used to highlight the laminate failure scenario during residual compression tests. Finally, the impact energy effect on the residual strength is evaluated and compared to experimental results.

Mots clés: Impact damage; Composite; Damage tolerance; CAI

Domaines: Matériaux

Samuel Rivallant, Christophe Bouvet, Natthawat Hongkarnjanakul. Failure analysis of CFRP laminates subjected to Compression After Impact: FE simulation using discrete interface elements. Composites Part A: Applied Science and Manufacturing, 2013, vol. 55, pp. 83-93. ⟨10.1016/j.compositesa.2013.08.003⟩. ⟨hal-00869432⟩