Zirconia-spinel composites. Part I: synthesis of powders and dense materials

Olivier Quénard (1) , Christophe Laurent (1) , Alain Peigney (1) , Abel Rousset (1)

1 CIRIMAT - Centre interuniversitaire de recherche et d'ingenierie des matériaux

MgAl2O4 and x wt% ZrO2-MgAl2O4 (1 # x # 30) composite powders were prepared by the urea combustion route. The powders were further ground by either ball milling or attrition to refine the grain size. Zirconia was found solely in the tetragonal form. Dense materials were prepared by hot pressing. The spinel matrix grains were submicronic in size. The ZrO2 particles were homogeneously dispersed at the grain junctions of the matrix, and their average size increased from less than 0.20 mm to ca. 0.45 mm with increasing content of ZrO2. The formation of monoclinic ZrO2 particles proceeded accordingly, being easier in materials with a finer matrix grain size (ex-attrition).

Mots clés: Zirconia; Spinel; Composites

Domaines: Matériaux

Olivier Quénard, Christophe Laurent, Alain Peigney, Abel Rousset. Zirconia-spinel composites. Part I: synthesis of powders and dense materials. Materials Research Bulletin, 2000, vol. 35, pp. 1967-1977. ⟨10.1016/S0025-5408(00)00410-4⟩. ⟨hal-00950063⟩