Morphology and dynamical mechanical properties of poly ether ketone ketone (PEKK) with meta phenyl links

Abstract : Poly ether ketone ketone (PEKK) with different proportion of meta phenyl links were investigated by combining differential scanning calorimetry and dynamic mechanical analysis. The influence of the Terephthalyl/Isophthalyl isomers (T/I) ratio on the vitreous phase is mild, the shift of the glass transition is limited to a few degrees and the vitreous G0 is only sensitive to the content of the crystalline phase. Contrarily, the increase of meta isomers is responsible for a significant decrease of the melting temperature (Tm) by 60 8C, which considerably facilitates processing. The modification of interchain interactions in the crystalline phase might be implied. A series of thermal protocols evidenced that the difference of crystallization behavior is also dependent upon the T/I isomer ratio. A time and temperature dependence of annealing on the double melting behavior of PEKK was observed. Regarding the mechanical behavior, the observed reinforcing effect due to the crystalline phase was more prominent in the rubbery state than in the glassy state.
Document type :
Journal articles
Complete list of metadatas

Cited literature [15 references]  Display  Hide  Download

https://hal.archives-ouvertes.fr/hal-01345998
Contributor : Open Archive Toulouse Archive Ouverte (oatao) <>
Submitted on : Monday, July 18, 2016 - 10:23:51 AM
Last modification on : Thursday, October 24, 2019 - 11:38:04 AM

File

quiroga_cortes_15717.pdf
Files produced by the author(s)

Identifiers

Collections

Citation

Luis Quiroga Cortes, Nicolas Caussé, Eric Dantras, Antoine Lonjon, Colette Lacabanne. Morphology and dynamical mechanical properties of poly ether ketone ketone (PEKK) with meta phenyl links. Journal of Applied Polymer Science, Wiley, 2016, vol. 133 (n° 19), pp. 1-10. ⟨10.1002/app.43396⟩. ⟨hal-01345998⟩

Share

Metrics

Record views

153

Files downloads

778