Study of degradation mechanisms of black anodic films in simulated space environment

Abstract : Black anodic films are used on aluminium alloys in space applications to provide specific thermo-optical properties to the surface. During the process, thermal and/or residual stresses can lead to crazing of the film in particular conditions. After thermal cycling performed to simulate the space environment, cases of film flaking have been observed. This constitutes potential risks for the satellite lifetime. Peel-test and scratch-test have been used to evaluate the evolution of the adhesion during ageing. For example, we showed that this phenomenon is due to crack propagation occurring at the beginning of ageing. A finite element model has then been developed to study more accurately the propagation mode of these cracks. Thermal stresses are likely to propagate cracks through the film in pure opening mode. When cracks are long enough, thermal stresses can generate propagation parallel to the interface. This would result in the decrease of the measured adhesion with a possibility of flaking.
Complete list of metadata

Cited literature [12 references]  Display  Hide  Download
Contributor : Open Archive Toulouse Archive Ouverte (oatao) <>
Submitted on : Tuesday, July 31, 2018 - 10:50:47 AM
Last modification on : Wednesday, June 24, 2020 - 4:18:55 PM
Long-term archiving on: : Thursday, November 1, 2018 - 12:35:14 PM


Files produced by the author(s)


  • HAL Id : hal-01851864, version 1
  • OATAO : 3111


Yann Goueffon, Muguette Monjauze, Catherine Mabru, Laurent Arurault, Claire Tonon, et al.. Study of degradation mechanisms of black anodic films in simulated space environment. 11th International Symposium on Materials in Space Environment, Sep 2009, Aix-en-Provence, France. pp.0. ⟨hal-01851864⟩



Record views


Files downloads