Characterization of typical patinas simulating bronze corrosion in outdoor conditions

Giulia Masi (1) , Jérôme Esvan (2) , Claudie Josse (3) , Cristina Chiavari (1) , Elena Bernardi (1) , Carla Martini (1) , Maria Chiara Bignozzi (1) , Nina Gartner (4) , Tadeja Kosec (4) , Luc Robbiola (5)

1 UNIBO - Alma Mater Studiorum Università di Bologna = University of Bologna
2 CIRIMAT - Centre interuniversitaire de recherche et d'ingenierie des matériaux
3 Centre Castaing - Centre de microcaractérisation Raimond Castaing
4 ZAG - Slovenian National Building and Civil Engineering Institute = Zavod za gradbeništvo Slovenije
5 TRACES - Travaux et recherches archéologiques sur les cultures, les espaces et les sociétés

In order to bring the treatment of historical bronze monuments in line with proper engineering practice and cultural heritage regulations, the standardisation of artificially aged surfaces that are comparable with natural ones is still to take place. In this aim, this investigation reports a comparative study of corroded quaternary bronze samples produced by accelerated ageing tests, simulating the unsheltered and sheltered exposure conditions mainly affecting outdoor bronze monuments. The effects of run off in a dropping test (unsheltered simulation) and the exposure to stagnant acid rain in a wet & dry test (sheltered simulation) on a bronze surface were studied. A multi-analytical approach was performed including conventional analytical methods, such as a microscopy examination coupled with elemental and structural analyses of the surface. In addition, a focused ion beam (FIB) was used to produce cross sections in the size range up to a few tens of nanometres. It is evidenced that the corrosion layers, forming a nano-porous structure, are linked to a decuprification process marked by the preferential dissolution of Cu and Zn and the formation of a Sn-O species network within the barrier layer. A correlation between the tin content of the alloy and the corrosion amplitude is shown: the anodic areas are related to the lowest tin-content part of the alpha phase (in the centre of the dendrite), while the eutectoid areas (including the delta phase) are cathodic and therefore not attacked. The corroded samples artificially aged are well representative of natural corrosion structures observed on outdoor bronzes. (C) 2017 Elsevier B.V. All rights reserved.

Mots clés: FIB; Atmospheric corrosion; Nano-porous corrosion layer; Bronze; Artificial ageing

Domaines: Matériaux

Giulia Masi, Jérôme Esvan, Claudie Josse, Cristina Chiavari, Elena Bernardi, et al.. Characterization of typical patinas simulating bronze corrosion in outdoor conditions. Materials Chemistry and Physics, 2017, 200, pp.308-321. ⟨10.1016/j.matchemphys.2017.07.091⟩. ⟨hal-01997535⟩